Einfluss von Calciumnitrat
auf den Frost-Tau-Widerstand von Beton

Figure: Yara/CBM

Versuchsablauf

Figure: Yara/CBM

Prüflösungsaufnahme aller Betonmischungen

Figure: Yara/CBM

Ein Probenkörper aus „8 % CN“-Beton vor (links) und nach (rechts) Frost-Tau-Angriff

Figure: Yara/CBM

Menge der Abplatzungen aller untersuchten Betone

Figure: Yara/CBM

Relativer dynamischer E-Modul beim „Referenz“-Beton während des CDF-Tests

Figure: Yara/CBM

Luftporengrößenverteilung beim Festbeton

Figure: Yara/CBM

Dr.-Ing. Wolfgang Franke, Yara Industrial Porsgrunn/Norway

Since 2003 Senior Engineer with scientific experience in environmental and construction engineering; 2004 bis 2009 as scientific project engineer in research, development and education about environmental engineering at Kassel University; Germany; since 2009 (additionally) involved in faculty management and development. Manager of technical development within Yara Industrial, and based at Yara’s Research Centre in Porsgrunn, Norway. Focus is on technical development and market support for concrete admixtures, waste water treatment and biogas technology.

Dipl.-Ing. Charlotte Thiel; Technische Universität München

Studies of building materials engineering at the Technical University of Munich; research assistant in the working group „concrete technology“ at the Center for Building Materials and Material Testing (cbm) of the Technical University of Munich since 2008; research focus: transport processes in concrete as well as sustainability and durability of concrete

Civil Eng. Francisco Durán; Technische Universität München

Studies of civil engineering at Universidad de La Serena in La Serena, Chile; continued studies at Ruhr University Bochum within a scholarship granted by DAAD in 2006; from 2009 to 2011 trainee and project specialist at RAG Deutsche Steinkohle in Herne, afterwards engineer of special projects at FLUOR S.A. in Santiago de Chile; from 2012 to 2014 research assistant of the working group „concrete technology“ at the Center of Building Materials and Material Testing of TUM

Prof. Dr.-Ing. Christoph Gehlen; Technische Universität München

Studies of civil engineering and surveying; he completed his doctorate at RWTH Aachen in 2000; Chair at Materials Science and Testing in Civil Engineering at the Technical University of Munich (TUM) since 2008 and head of cbm (Center of Building Materials and Material Testing); partner of an international engineering firm; his research focuses on the service life of mineral and metallic building materials

In dieser Studie wird der Einsatz von Luftporenbildner in Kombination mit Calciumnitrat untersucht. Beides sind übliche Zusatzmittel, die beim Betonieren in kalter Witterung gemäß ACI 306 (2002) Verwendung finden. Schließlich kann der kombinierte Einsatz der beiden Zusatzmittel zu einer höheren Dauerhaftigkeit und Druckfestigkeit von Betonprodukten in kalten Umgebungen führen.

Kurzfassung

Beton ist bei kalter Witterung während der Betonierung nicht nur niedrigen Temperaturen ausgesetzt, sondern auch Frost-Tauwechseln über die gesamte Standzeit. Daher muss nicht nur die Betonproduktion an die Umweltbedingungen angepasst werden, vielmehr muss auch die Rezeptur dauerhaft sein und den Umwelteinflüssen standhalten. Im Allgemeinen wird ein Luftporenbildner eingesetzt, um das kapillare Porensystem zu unterbrechen und so dem gefrierenden Wasser weitere Ausdehnungsbereiche zu verschaffen. Ein Verlust an Druckfestigkeit ist der Nachteil dieser Methode. Im Rahmen dieses...